| Kinematic Viscosity, mm2/s (cSt) |
|
|
|
| 100°C |
1.65 min |
1.68 |
ASTM D445 |
| 40°C |
5.0 min |
5.0 |
ASTM D445 |
| -40°C |
300 max |
261 |
ASTM D445 |
| -54°C |
|
|
ASTM D2532 |
| 1.5 hours, initial |
1300 max |
1,078 |
|
| 3.0 hours |
1300 max |
1,100 |
|
| Dielectric strength, kV |
35 min |
40 |
ASTM D877 |
| Resistivity at 25°C, ohm-cm |
1.0 x 1010 min |
2.1 x 1013 |
ASTM D1169 |
| Flash point, °C |
150 min |
172 |
ASTM D92 |
| Fire point, °C |
160 min |
178 |
ASTM D92 |
| Acid number, mg KOH/g |
0.20 max |
0.01 |
ASTM D664 |
| Water, mg/kg (ppm) |
50 max |
26 |
ASTM D6304 |
| Rubber swell, SAE AMS 3217/2 (NBR-L), percent change in volume |
0.0 - 10% |
7.4% |
ASTM D4289 |
| Solid particle contamination |
|
|
Paragraph 4.4.1 |
| Particle count per size range NAS 1638 |
|
|
FTM 3012 |
| 5 to 15 |
8000 max |
417 |
|
| 16 to 25 |
1425 max |
27 |
|
| 26 to 50 |
253 max |
30 |
|
| 51 to 100 |
45 max |
0 |
|
| > 100 |
8 max |
0 |
|
| AS4059 Contamination Class |
5 max |
2 |
|
| Storage stability |
PASS |
PASS |
FTM 3465 |
| High-temperature stability |
PASS |
PASS |
Paragraph 4.4.3 |
| Corrosiveness and oxidation stability |
|
|
ASTM D4636 |
| Change in acid number, mg KOH/g |
0.5 max |
0.00 |
|
| Metal specimen weight change, mg/cm2 |
|
|
|
| Aluminum |
± 0.2 |
-0.01 |
|
| Cadmium plated steel |
± 0.2 |
0.00 |
|
| Copper (copper color) |
± 0.4 (3a max.) |
0.01 (3a) |
|
| 1010 Steel |
± 0.2 |
0.01 |
|
| Magnesium |
± 0.2 |
0.00 |
|
| Percent change in viscosity at 40°C |
5% max |
1.2% |
|
| Separation of insoluble materials or gumming of the fluid |
None |
None |
|
| Compatibility |
PASS |
PASS |
Paragraph 4.4.2 |